The effect of process conditions on the performance of epitaxial InP solar cells

摘要

Indium phosphide solar cells have a higher resistance to electron irradiation than Si or GaAs cells of comparable junction depth. As a result, there is much interest in the use of this material for space applications. Cells of this material were made in bulk InP by a number of techniques, including ion implantation, direct diffusion in sealed ampoules, and by open tube diffusion. However, it is generally considered that the epitaxial approach will be superior to all of these techniques. The epitaxy of InP is considerably more difficult than that of gallium arsenide, for a number of reasons. Perhaps the most important is the fact that the native oxides of Indium are extremely difficult to remove, as compared to that of Gallium. In addition, thermal treatments for the desorption of these oxides often result in the formation of phosphorus vacancies and free indium on the surface. Thus, inadequate sample preparation before epitaxy, poor reactor cleaning procedures, or poor transition procedures between the growth of successive layers, all give rise to trap phenomena and to high interface recombination velocities. Moreover, the lifetime of the grown material is dominated by the occurrence of native defects, so that it is a strong function of growth parameters. These problems are of special interest to the fabrication of solar cells, where long life-time, combined with the absence of traps, is highly desirable. A study of this problem is described using a non-invasive diagnostic technique which was developed.