Fracture toughness and crack resistance curves for fiber compressive failure mode in polymer composites under high rate loading

摘要

This work presents an experimental method to measure the compressive crack resistance curve of fiber-reinforced polymer composites when subjected to dynamic loading. The data reduction couples the concepts of energy release rate, size effect law and R-curve. Double-edge notched specimens of four different sizes are used. Both split-Hopkinson pressure bar and quasi-static reference tests are performed. The full crack resistance curves at both investigated strain rate regimes are obtained on the basis of quasi-static fracture analysis theory. The results show that the steady state fracture toughness of the fiber compressive failure mode of the unidirectional carbon-epoxy composite material IM7-8552 is 165.6 kJ/m(2) and 101.6 kJ/m(2) under dynamic and quasi-static loading, respectively. Therefore the intralaminar fracture toughness in compression is found to increase with increasing strain rate.