Preparation of Bp Single Crystals by High Pressure Flux Method

摘要

Single crystals of BP, a III-V compound semiconductor, were obtained by the high pressure flux method. Cu3P and Ni12P5 powders were used as the flux, and mixed with BP powder. Two kinds of mixtures were prepared: (1) 1.8g (BP) + 35 G (Cu3P) and (2) 1.7 g (BP) + 25 g (Ni12P5). They were compressed into pellets, heated at 1300 C for 24 h in an induction furnace under a pressure of 1 MPa using Ar-P2 gas, and slowly cooled to room temperature. In case (1), BP single crystals grew along the (III) plane, and in case (2) they grew as an aggregate of crystallites. The cathodoluminescence spectra of the synthetic BP crystals showed peaks near 680 nm (1.82 eV) for case (1), and 500 nm (2.47 eV) for case (2). By using the high pressure flux method conventional sized crystals were obtained in a relatively short time.