Effect of High-Temperature Annealing on the Microstructure and Thermoelectric Properties of GaP Doped SiGe

摘要

Annealing of GaP doped SiGe will significantly alter the thermoelectric properties of the material resulting in increased performance as measured by the figure of merit Z and the power factor P. The microstructures and corresponding thermoelectric properties after annealing in the 1100 to 1300 C temperature range have been examined to correlate performance improvement with annealing history. The figure of merit and power factor were both improved by homogenizing the material and limiting the amount of cross-doping. Annealing at 1215 C for 100 hr resulted in the best combination of thermoelectric properties with a resultant figure of merit exceeding 1x10 to the -3 deg C to the -1 and a power factor of 44 microW/cm/deg C sq for the temperature range of interest for space power: 400 to 1000 C.