Conversion of polymers of methyl- and vinylsilane to Si-C ceramics

摘要

Poly(methylsilane) and poly(vinylsilane) were synthesized using a titanocene catalyst, and their pyrolytic conversion to ceramics was followed using a combination of thermal analysis and infrared spectroscopy. The two polymers have distinctly different backbone structures, as determined by Si NMR; methylsilane polymerizes to a polysilane, while vinylsilane polymers have predominately polycarbosilane backbone, with some polysilane structure as well. The pyrolysis path and char yield were dependent primarily on backbone structure, with little influence of polymer molecular weight. The majority of the weight loss on conversion occurs below 650 degrees C, although bond rearrangement continues to 1400 degrees C. Poly(vinylsilane) produced a C-rich Si-C ceramic in which the carbon was dispersed on a sufficiently fine level to show resistance to oxidation on heating in air to 1400 degrees C.