Nondestructive Determination of Heat/Fire Damage to Polymer- Matrix Composites Using Obliquely Insonified Ultrasonic Waves

摘要

Heat and fire damage to composite structures cause loss of strength that cannot be detected by current NDE methods unless physical damage occurs. Further, there is a lack of fundamental understanding of the mechanism of damage from thermal exposure of organic matrix composites to elevated temperatures. Information compiled from field reports and lab experiments increasingly suggests that there is material degradation and it is not necessarily involved with the introduction of physical defects. In recent years, various researchers examined the potential to identifying thermal degradation to organic matrix composites prior to delamination. The methods that were used include: ultrasonics, backscattered X-ray, eddy current, thermography, drift and LPF spectroscopies, acousto-ultrasonics and hardness testing. None of these methods were able to correlate NDE results with loss of mechanical properties.