Applying cold sintering process to a proton electrolyte material: CsH2PO4

摘要

The Cold Sintering Process (CSP) was applied to CsH2PO4, a proton conducting electrolyte. The powders were sintered between 120 degrees C and 200 degrees C under 300 MPa for 1 h and the ceramics investigated for their respective structure-property-process relations. The microstructure development of the CsH2PO4 materials was characterized for grain size, and dihedral angle distributions for a variety of the CSP processing conditions. The electrical properties of the cold sintered CsH2PO4 were characterized through electrochemical impedance spectroscopy over a temperature range between 120 degrees C and 200 degrees C. The data suggests that the proton conductivity is 2.30 x 10(-4) Scm(-1) at 200 degrees C with good repeatability during cycled measurements.