Interpenetrating polymer networks derived from epoxide-amine adducts in either polymer network

摘要

A new type of interpenetrating polymer network was synthesized via photoinitiated free-radical polymerization of α,ω-methacryloyl terminated macromonomers prepared from epoxide-amine-adducts, followed by thermal addition polymerization of bis-phenol-A diglycidyl ether and 4,4′-diaminodiphenylsulfone or 3(4),8(9)-bis(amino-methyl)tricyclo[5.2.1.0.]decane. The interpenetrating polymer networks are optically transparent and show only one glass transition temperature ranging from -10 to 130℃, as a function of the macromonomer/addition polymer mixing ratio. The presence of a single phase was confirmed by scanning electron microscopy (SEM).%Ein neuer Typ eines interpenetrierenden Polymer-Netzwerkes (IPN) wurde durch radikalische (photochemische) Polymerisation von α,ω-methacryloyl-terminierten Epoxid-Amin-Makromonomeren, kombiniert mit nachfolgender thermischer Additionspolymerisation von Bisphenol-A-diglycidylether und 3(4),8(9)-Bis(aminomethyl) tricyclo[5.2.1.0.]decan bzw. 4,4′-Diaminodiphenylsulfon, erhalten. Die interpenetrierenden Polymer-Netzwerke weisen, in Abhängigkeit vom Anteil des Makromonomeren und des Additionspolymeren, nur eine Glasübergangstemperatur zwischen -10 und 130℃ auf. Die IPN sind optisch klar und zeigen auch im Rasterelektronenmikroskop (REM) keine Phasenseparation.