To reduce the production cost of Bi-2223 superconducting tapes, Bi-2223/Ag/Ni tapes were fabricated by the powder-in-tube process. The effect of heat treatment on the microstructure and critical current of the Bi-2223/Ag/Ni tapes were studied. The phase compositions of the samples were characterized using XRD. The microstructure was observed using SEM. Experimental results indicate that higher temperature is more conducive to the formation of Bi-2223 phase at an atmosphere of 8.5% O 2 . After the two-step heat treatment, the critical current of samples is about 67.5 A.