Samples from the center of plates of rolled aluminum alloys AA 8090 and 7055 were investigated using microbeam diffraction and polychromatic synchrotron x-ray radiation. Transmission Laue patterns from different parts of the samples were compared and analyzed for the presence of mesotexture similar to that observed previously in the center of plates of aluminum alloy AA 2090 (i.e., near single-crystal volumes of 5 to 10 or more adjacent grains with nearly identical orientation). The macrotexture and grain morphology of the AA 8090 samples were quite similar to those of samples of AA 2090; the macrotexture and grain morphology of the AA 7055 sample differed from those of AA 2090. Approximately 10% of the AA 8090 volume consisted of material with the near single-crystal mesotexture (compared to about 40% typical for AA 2090) while no near single-crystal volumes were observed in the AA 7055 material.
展开▼
机译:使用Microbeam衍射和多色同步rotron X射线辐射研究来自轧制铝合金AA 8090和7055的板中心的样品。比较来自样品的不同部位的传输Laue模式,并分析与先前在铝合金AA 2090的板的中心(即,在5至10个或更多相邻颗粒的单晶体积附近的单晶容积附近观察到的Mesotexture的延伸构件的存在和分析几乎相同的方向)。 AA 8090样品的宏观纹理和晶粒形态与AA 2090的样品非常相似; AA 7055样品的Macrotexture和晶粒形态与AA 2090的样品不同。大约10%的AA 8090体积由具有近单晶性介质构成的材料(与AA 2090的典型约40%相比),同时没有近单个在AA 7055材料中观察到晶体体积。
展开▼