Metallization of Iron Ores with Solid Reductants

摘要

Research on the solid-fuel reduction of Knob Lake iron ores was conducted to upgrade lean and high-grade ores and recover metallized products suitable for ironmaking or steelmaking. The program included bench-scale tests plus a number of continuous campaigns in a 34-inch by 36-foot rotary kiln. In the laboratory, metallizations in excess of 90 percent were achieved by reduction of crushed ore with lignite at 950C. Subsequent grinding (to minus 200 mesh) and wet magnetic separation yielded concentrates analyzing less than 3.0 percent SiO2 and more than 90 percent Fe. Virtually complete recovery of the iron occurred. During early continuous tests the crushed ore created a serious ringing in the kiln which was solved by balling the fines with bentonite. Unfortunately, at this temperature (950C) the bentonite militates against the concentratability of the metallized product. For example, a run on direct-shipping ore produced concentrates of 89.5 percent Fe and 4.5 percent SiO2. At 900C the adverse effect of bentonite disappeared and concentrates of 88.4 percent Fe and only 2.5 percent SiO2 resulted. However, with comparable feed rates, the metallization dropped to 73 percent. (Author)