Comparative M-H characteristics of 1-5 and 2-17 type samarium-cobalt permanent magnets to 300 C

摘要

Recent consideration of the use of permanent magnets in space power converters at heat rejection temperatures exceeding 250 C and in miniature high temperature actuators is supporting a search for permanent magnets resistant to demagnetizing forces at high temperature. The present paper investigates the short-term demagnetization resistance to applied bucking fields and at temperatures up to 300 C of SmCo5 type magnets, in the form of 1-cm cubes, from several commercial sources. Quasistatic, 2nd quadrant M-H data taken at selected temperatures are the source of derived plots which are then compared to similar data for previously tested Sm2Co17 type magnets. The 1-5 magnet remanence tends to be about 1.5 kG below that of the 2-17 magnets throughout the temperature range. However, the intrinsic coercivities and M-H curve 'knee-fields' seen in particular 1-5 magnets were considerably above those seen previously in the 2-17 magnets. This superior resistance to demagnetizing fields attainable in 1-5 magnets is also illustrated by safe operating area plots based on the knee-field, the magnetic induction swing and temperature. Comments are made on the possibility that a remanence versus knee-field tradeoff can make 1-5 material competitive with 2-17 in applications where a magnet has to withstand large bucking fields at high temperature.