The Effect of Sliding Speed on Film Thickness and Pressure Supporting Ability of a Point Contact Under Zero Entrainment Velocity Conditions

摘要

A unique tribometer is used to study film forming and pressure supporting abilities of point contacts at zero entrainment velocity (ZEV). Film thickness is determined using a capacitance technique, verified through comparisons of experimental results and theoretical elastohydrodynamic lubrication (EHL) predictions for rolling contacts. Experiments are conducted using through hardened AISI 52 100 steel balls, Polyalphaolefin (PAO) 182 and Pentaerythritol Tetraheptanoate (PT) lubricants, and sliding speeds between 2.0 to 12.0 m/s. PAO 182 and PT are found to support pressures up to 1. 1 GPa and 0.67 GPa respectively. Protective lubricant films ranging in thickness between 90 to 2 10 nm for PAO 182 and 220 to 340 nm for PT are formed. Lubricants experience shear stresses between 14 to 22 MPa for PAO 182 and 7 to 16 MPa for PT at shear rates of 10(exp 7)/sec. The lubricant's pressure supporting ability most likely results from the combination of immobile films and its transition to a glassy solid at high pressures.