Effect of Hydrogen Annealing on the Oxidation Resistance of Four EPM Single Crystal Superalloys

摘要

Four single crystal EPM (enabling propulsion materials) developmental airfoil superalloys were hydrogen annealed at 1300 C for up to 100 hours to remove sulfur and improve oxidation resistance. Although the 1100 and 1150 C cyclic oxidation resistance was remarkably improved by annealing for 24 or 100 hours, the behavior was still considerably inferior to that of commercially available single crystal superalloys, especially those that are either Y-doped or hydrogen annealed. Excessive degradation in the developmental alloys appeared to be correlated with low Cr contents and, to a lesser extent, high Co and Re contents.