Effect of annealing on Curie temperature and phase transition in La0.55Sr0.08Mn0.37O3 epitaxial films grown on SrTiO3 (100) substrates by reactive radio frequency magnetron sputtering

摘要

Mn-poor LaSrMnO3 (LSMO) epitaxial films were grown on SrTiO3 (100) substrates by radio frequency magnetron sputtering in an argon and oxygen gas mix, and then the samples were annealed in air at various temperatures (T-a). 2 theta-chi X-ray diffraction mapping, nano-beam diffraction analysis through transmission electron microscopy, and electron back scatter diffraction through scanning electron microscopy revealed that -the crystal symmetry of the LSMO films changed from monoclinic/orthorhombic to rhombohedral on annealing in air. Curie temperature (T-C) of the LSMO films was found to increase with increasing T-a, and become higher than the room temperature at T-a >= 861 degrees C, indicating that the cause of these changes was the filling of oxygen and the transition of the crystal symmetry into rhombohedral. (C) 2016 Elsevier Inc. All rights reserved.