Dynamic Infrared Study of Polyphenylene Sulfide Using Planar Array Infrared Spectroscopy

摘要

Planar array infrared (PA-IR) spectroscopy was used to study poly-phenylene sulfide (PPS) at room temperature during the application of a sinusoidal elastic deformation. All of the intensity in the dynamic spectra was contained within the in-phase spectrum, which was expected since the measurements were carried out at room temperature, far below the glass transition temperature. The contributions of chain orientation, sample thinning, and stress-induced band shifts were separated in the dynamic spectra. It was found that the effects of chain orientation and sample thinning canceled each other out. Stress-induced band shifts far below the spectral resolution, on the order of 0.01 cm~(-1), were quantified and used to calculate the stress optical coefficients and mode Gruneisen parameters for PPS.