Stability of Skutterudite Thermoelectric Materials

摘要

By multifilling with La, Ba, Ga, Ti, Yb, Ca, Al, and In, the dimensionless figure of merit ZT of filled skutterudites has been improved in this work. ZT reached 0.75 for p-type (La,Ba,Ga,Ti)_x(Fe,Co)_4Sb_(12) (x = 0.8 to 1.0) and 1.0 for n-type (Yb,Ca,Al,Ga,In)_y(Co,Fe)_4Sb_(12) (y = 0.7 to 0.9). After annealing at 873 K for 180 h, 300 h, 710 h, 1000 h, and 5000 h in vacuum, the Seebeck coefficient S and the electrical resistivity ρ of the samples increased while the thermal conductivity λ decreased with increasing annealing time. As a result, the ZT values of both p- and n-type skutterudites remained unchanged or were slightly improved, demonstrating the excellent thermal stability of these skutterudites.