Magnetic properties and microwave absorption in Ni-Zn and Mn-Zn ferritenanoparticles synthesized by low-temperature solid-state reaction

摘要

In this work, Mn_0.7Zn_0.3Fe_2O_4 and Ni_0.7Zn_0.3Fe_2O_4 nanoparticles with super-paramagnetic properties and size distribution from 10 to 52 nm were investigated. These particles were produced by a low-temperature solid-state reaction method without the ball-milling process. The size and morphology of the nanocrystallites were determined by X-ray diffraction, transmission electron microscopy and scanning tunneling microscopy methods. Magnetic measurements such as alternating gradient field magnetometers were used to justify the super-paramagnetic properties of these nanoparticles. Their microwave absorption in the range of 8-18 GHz was studied by a vector network analyzer. Responses of the device under tests were studied. Also, the percentage of the resin, the size and thickness of the mount were determined. The band width of 2.3 GHz was obtained with reflection-loss/written-loss of -16 dB around 10.4 GHz.