Influence of preparation conditions on the dispersion parameters of sprayed iron oxide thin films

摘要

Iron oxide thin films were prepared by spray pyrolysis technique (SPT) at various substrate temperatures (T_(sub)) and different deposition time. X-ray diffraction (XRD) analysis showed that, at T_(sub) ≥ 350℃, a single phase of α-Fe_2O_3 film is formed which has the rhombohedral structure. Moreover, the crystallinity was improved by increasing T_(sub). The effect of T_(sub) as well as deposition time on the optical dispersion of these films has been investigated. The optical transmittance and reflectance measurements were performed by using spectrophotometer in the wavelength range from 300 to 2500 nm. The refractive index was determined by using Murmann's exact equation. It was observed that, the refractive index increased with increasing in both the T_(sub) and film thickness. The optical dispersion parameters have been evaluated and analyzed by using Wemple-Didomenico equation. The obtained results showed that, the dielectric properties have weak dependencies of growth temperature and film thickness. At T_(sub) ≥ 350℃, the average values of oscillator energy, E_o and dispersion energy, E_d were found to be 5.96 and 34.08 eV. While at different thickness, the average values of dispersion energies were found to be 3.93 and 17.08 eV. Also, the average values of oscillator strength S_o and single resonant frequency ω_o were estimated 10.78 × 10~(13) m~(-2) and 5.99 × 10~(15) Hz, while at different thickness were evaluating 4.81 × 10~(13) m~(-2) and 6.11 × 10~(15) Hz. Furthermore, the optical parameters such as wavelength of single oscillator λ_o, plasma frequency ω_p, and dielectric constant ε have been evaluated. The carrier concentration N_(opt) by using Drud's theory was obtained the range of 5.07 × 10~(25) m~(-3) to 1.04 × 10~(-26) m~(-3).