Control of crystalline phases in magnetic Fe nanoparticles inserted inside a matrix of porous carbon

摘要

Two magnetic composites made up of Fe nanoparticles (Fe-NPs) embedded in a porous amorphous carbon matrix are presented. One of the samples, Fe-S-AC was obtained with the aid of sucrose and the other, Fe-AC, in the absence of this substance. The XRD patterns show Bragg diffraction peaks associated with α-Fe and γ-Fe crystalline phases in the Fe-AC sample, while only peaks corresponding to the α-Fe phase are observed for Fe-S-AC powders. The Fe-NPs exhibit broad particle-size distributions for both samples, 5-50 nm for Fe-AC, whereas two populations (2-8 and 10-70 nm) for the Fe-S-AC composite are found. This fact gives rise to poorly defined blocking temperatures, as it can be deduced from the broad maxima observed in M_(ZFC)(T) variations. In addition, M(H) curves for both Fe-AC and Fe-S-AC samples reveal the existence of exchange-bias effect for T<60K, probably due to a magnetic coupling within a core/shell structure of the Fe-NPs, although this effect was observed to be less significant for Fe-S-AC.