The new composites of carbon nanotube with silicon dioxide (SiO{sub}2) nanopartical for FED cathode is studied, It has significantly improved emission current density property and stable emission characterization of cathode, because it has higher enhancement factor and less shield-effect by adjusting silicon nanopartical content. The results indicated that when about 80wt % CNT is optimum content, the current density at the electric field 2 V/μm is 56mA/mm{sup}2, the turn-on field of the CNTs cathode was about 0.71V/μm. The fluctuation of emission current is less than 3% for three hours.