Process for producing grain-oriented thin electrical steel sheet having high magnetic flux density by one-stage cold-rolling method

摘要

The present invention provides a grain-oriented electrical steel sheet having a thickness of up to 0.17 mm and excellent product magnetic characteristics. The present invention is characterized in that a silicon containing acid-soluble Al, N and Sn is used as the starting material, the N and acid-soluble Al contents in the slab are adjusted to 0.0050 to 0.0100% and {(27/14) x N (%) + 0.0035} to {(27/14) x N (%) + 0.0100}%, respectively, the thickness of the hot-rolled sheet is adjusted so that the thickness reduction ratio at the one-stage cold-rolling is 85 to 92%, and the Nas AlN content in the hot-rolled steel sheet is controlled to 0.0005 to 0.0020%.