This invention provides a process for preparing a powder of aluminum titanate, comprising the steps of subjecting to pressure molding a mixture of 100 parts by weight of a mixture of A12O3 and TiO2 at a molar ratio of the former : the latter of 1 : 0.95-1.05, 2 to 5 parts by weight of SiO2, 2 to 5 parts by weight of iron oxide calculated as Fe2O3 and 1 to 3 parts by weight of a powder of an organic substance; sintering the molded product at a temperature of 1600 to 1700.degree.C in a closed container; and pulverizing the molded product, and also provides a process for preparing a sintered body of aluminum titanate, comprising the steps of molding the powder of aluminum titanate obtained by the above-mentioned process and sintering the molded product at 1450 to 1550.degree.C.
展开▼
机译:本发明提供了一种制备钛酸铝粉末的方法,该方法包括以下步骤:将前者:后者的摩尔比为1∶0.95-的100重量份的Al 2 O 3和TiO 2的混合物进行压力模塑。 1.05、2至5重量份的SiO 2,2至5重量份的以Fe 2 O 3计的氧化铁和1至3重量份的有机物质粉末;在密闭容器中在1600至1700℃的温度下烧结模制品;本发明还提供一种制备钛酸铝烧结体的方法,该方法包括以下步骤:将通过上述方法获得的钛酸铝粉末成型,并在1450至1550°C的温度下烧结该成型品。 。
展开▼