Process for preparing aluminum titanate powder and sintered body
Process for preparing aluminum titanate powder and sintered body
展开▼
机译:钛酸铝粉及烧结体的制备方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
A process for preparing a powder of aluminum titanate, including the steps of subjecting to pressure molding a mixture of 100 parts by weight of a mixture of Al2O3 and TiO2 at a molar ratio of the former: the latter of 1:0.95-1.05, 2 to 5 parts by weight of SiO2, 2 to 5 parts by weight of iron oxide calculated as Fe2O3 and 1 to 3 parts by weight of a powder of an organic substance; sintering the molded product at a temperature of 1600 to 1700° C. in a closed container; and pulverizing the molded product. A further process for preparing a sintered body of aluminum titanate includes the steps of molding the powder of aluminum titanate obtained by the above-mentioned process and sintering the molded product at 1450 to 1550° C.
展开▼
机译:一种制备钛酸铝粉末的方法,该方法包括以下步骤:将100重量份的Al 2 Sub> O 3 Sub>和TiO < Sub> 2 Sub>的摩尔比为:后者为1:0.95-1.05,后者为SiO 2 Sub>的2至5重量份,氧化铁为2至5重量份以Fe 2 Sub> O 3 Sub>和1-3重量份有机物质粉末计算;在1600〜1700度的温度下烧结成型体。 C.在密闭的容器中;并粉碎成型产品。制备钛酸铝烧结体的另一种方法包括以下步骤:将通过上述方法获得的钛酸铝粉末成型,并在1450至1550℃下烧结成型品。 C。
展开▼