SYNTHESIS OF THE PHOSPHORESCENT PHOSPHOR OF STRONTIUM BARIUM ALUMINATES
SYNTHESIS OF THE PHOSPHORESCENT PHOSPHOR OF STRONTIUM BARIUM ALUMINATES
展开▼
机译:锶钡铝的磷的合成
展开▼
页面导航
摘要
著录项
相似文献
摘要
It relates to a manufacturing process of synthesizing a phosphor of - (referred to as barium aluminate or less strontium), Eu 2 +, Dy 3 + system: - The invention Sr 1 represents the yellow-green and cyan light emitting characteristic x Ba x Al 2 O 4 adding a starting raw material, SrCO 3, BaCO 3, Dy 2 O 3, and B 2 O 3 as a flux as the activator in the Al 2 O 3 as Eu 2 O 3, to study lubricant to synthesize a fluorescent material by solid-phase reaction. Sintering step of synthesizing a fluorescent substance was heat-treated for 3 hours with 1100~1400 ℃ temperature at 95% Ar + 5% H 2 in a reducing atmosphere. Ba addition amount is sikyeotgo change in the range of 0.0-1.0 mol, when the amount of Ba was added, the emission wavelength is 0.0-0.4mol yellow-green region, it turns when the light emission wavelength region an area close to the cyan, exceeds 0.5mol. In addition, the more the amount of Ba is increased field intensity of the luminescence and afterglow property represents the most excellent characteristics when the Ba was 0.1 mol was added. As a result of measuring the excitation and emission characteristics of the powder, the excitation spectrum is taking place here in a wide wavelength range of 250 ~ 450 nm, the emission spectrum shows a maximum peak at 480 ~ 520 nm.
展开▼
机译:本发明涉及一种合成-(Eu 2 +,Dy 3 Sup> +)-(Sub称铝酸钡或以下锶的)的荧光粉的制造方法。 1 Sub>表示黄绿色和青色发光特性 x Sub> Ba x Sub> Al 2 Sub> O 4 < / Sub>添加起始原料 SrCO 3,BaCO 3,Dy 2 Sub> Sub> Sub> O 3和B 2 Sub > O 3 Sub>作为助熔剂作为Al 2 Sub> O 3 Sub>中的活化剂,作为Eu 2 Sub> O 3, Sub>研究润滑剂通过固相反应合成荧光材料。合成荧光物质的烧结步骤在还原气氛中,在1100〜1400℃,95%Ar + 5%H 2 Sub>的条件下热处理3小时。 Ba的添加量为在0.0〜1.0mol的范围内的sikyeotgo变化,当Ba的添加量时,发光波长为0.0〜0.4mol的黄绿色区域,发光波长区域为接近青色的区域时变为。 ,超过0.5mol。另外,Ba的量越多,发光的场强度增加,并且当添加Ba为0.1mol时,余辉性质表示最优异的特性。测量粉末的激发和发射特性的结果是,激发光谱在250〜450 nm的宽波长范围内发生,发射光谱在480〜520 nm处显示出最大峰值。
展开▼