method of manufacturing a two-phase nanokompozytu (ti - zr) ni / pd to apply for anode material in the nickel hydride batteries (ni mh) is characterized by the fact that components of nanomaterial composite ti0,75zr0,25ni produces in the process of the mechanical synthesis involving mass mielniku00f3w d about weight powders 5: 1, in the atmosphere of argon, with elementsin the form of powders of titanium; nickel; in the form of filings generated by friction the zirconium.then the alloy subjected to heat treatment by wyu017carzaniu powders obtained in the process of mechanical synthesis at temperatures in the range of 700 - 800u00b0c / 0.5 h, favourably 750u00b0c / 0.5 h after which produces composite powders with nanokrystalicznych ti0,75zr0,25ni from 3 - 7%, preferably 5% agowymi palladium powder in the milling process.ratio of mielniku00f3w weight powder milling is 5: 1.