An austenitic cast iron according to the present invention is characterized in that: it comprises: basic elements comprising C, Si, Cr, Ni, Mn and Cu; and the balance comprising Fe, inevitable impurities and/or a trace-amount modifier element, which is effective in improving characteristic, in a trace amount; and it is an austenitic cast iron being a cast iron that is structured by a base comprising an Fe alloy in which an austenite phase makes a major phase in ordinary-temperature region; wherein said basic elements fall within compositional ranges that satisfy the following conditions when the entirety of said cast iron is taken as 100% by mass (hereinafter being simply expressed as "%"): C: from 2.0 to 3.0%; Si: from 4.0 to 5.4%; Cr: from 0.8 to 2.0%; Mn: from 3.9 to 5.6%; Ni: from 17 to 22%; and Cu: from 0.9 to 1.6%. It is an austenitic cast iron whose Ni content is less relatively, and is excellent in terms of oxidation resistance under high temperature and austenite-phase stability in intermediate-temperature region.