the subject of the invention is a manufacturing nanodendrytycznych particles of silver on the implant metal or metal ceramic, preferably titanium, in which to implant metal or metal - ceramic, preferably titanium, a porous structure by using metal urgii powders or anode oxidation.then implant immersed in elektrolicie temperature 15 - 20u00b0c, favourably 20u00b0c, which contains silver ions, and subjected to electrolytic deposition process katodowego nanodendrytu00f3w silver at cathode potential, preferably - iv potential circuit open. the duration of the process is dependent on the size of osadzanych particles advantageously 1 min.the electrolyte during the deposition nanodendrytu00f3w silver is mixed with stirrer speed of 30 - 50 rpm / min, preferably 50 r.p.m. after settling nanodendrytu00f3w silver surface implant metal or metal - ceramic washed with distilled water and dried in a stream of compressed gas, preferably nitrogen.