Effects of oxide additions and temperature on sinterability of milled silicon nitride

摘要

Specimens of milled alpha-Si3N4 with 0 to 5.07 equivalent percent of oxide additions were pressureless sintered at 1650 to 1820 C for 4 hours in nitrogen while covered with powdered Si3N4 SiO2. Densities of less than or equal to 97.5 percent resulted with approximately 2.5 equivalent percent of MgO, CeO2, Y2O3, and three mixtures involving these oxides. Densities of greater than or equal to 94 percent were obtained with approximately 0.62 equivalent percent of the same additives. At most temperatures, best sinterability (density maxima) was obtained with 1.2 to 2.5 equivalent percent additive.