Effect of Extreme Temperatures on the Elastic Properties and Fracture Behavior of Graphite/Polyimide Composites

摘要

The influence of elevated and cryogenic temperatures on the elastic moduli and fracture strengths of several C6000/PMR-15 and C6000/NR-15082 laminates was measured. Tests were conducted at -157 C, 24 C, and 316 C (-250 F, 75 F, and 600 F). Both notched and unnotched laminates were tested. The average stress failure criterion was used to predict the fracture strength of quasi-isotropic notched laminates.