Low Cycle Fatigue Behavior of Conventionally Cast Mar-M 200 at 1000 Deg C

摘要

The low cycle fatigue behavior of the nickel-based superalloy MAR-M 200 in conventionally cast form was studied at 1000 C. Continuous cycling tests, without hold times, were conducted with inelastic strain ranges of from 0.04 to 0.33 percent. Tests were also conducted which included a hold time at peak strain in either tension or compression. For the conditions studied, it was determined that imposition of hold times did not significantly affect the fatigue life. Also, for continuous cycling tests, increasing or decreasing the cycle frequency did not affect life. Metallographic analysis revealed that the most significant damage mechanism involved environmentally assisted intergranular crack initiation and propagation, regardless of the cycle type. Changes in the gamma morphology (rafting and rod formation) were observed, but did not significantly affect the failure.