Some Observations of Heated Gallium Arsenide Heteroface Solar Cells

摘要

GaAlAs/GaAs heteroface solar cells used in space offer advantages of higher operating temperatures and recovery from radiation damage using thermal annealing. Experiments were conducted to examine the effects on the room temperature photovoltaic properties of cells due to heating in a vacuum at temperatures encountered in radiation damage annealing. Some degradation of photovoltaic properties was observed for all the cells that were heated. The lifetime, due to heating, for a 20-percent degradation in output power was estimated for cells heated at 200 C and 400 C. The results for cells that were heated at 200 C for 1750 hours indicate a lifetime of at least 3 years. The results for cells that were heated at 400 C for 264 hours indicate that lifetimes in the range of 350 hours to 1400 hours may be expected. The results indicate that for cells that must be heated at 400 C the selection of fabrication techniques and materials is particularly important.