Stress Corrosion Evaluation of HP 9Ni-4Co-0.30C Steel Plate Welds

摘要

A stress corrosion cracking (SCC) investigation was conducted on HP 9Ni-4Co-0.30Csteel plate welds (welded by using straight polarity plasma arc and HP 9Ni-4Co-0.20C weld wire) since this material is being considered for use in the Advanced Solid Rocket Motor (ASRM) program. Prior to the welding, the material was double tempered at 538 C (1,000 F). After welding, only part of the material was stress relieved at 510 C (950 F) for 3 h. Round tensile specimens obtained from nonstress-relieved material were tested in 100-percent relative humidity at 38 C (100 F), in 3.5-percent NaCl alternate immersion, and in 5-percent salt spray at 35 C (95 F). Specimens obtained from stress-relieved material were tested in alternate immersion. The stress levels were 50, 75, and 90 percent of the corresponding 0.2-percent yield strength (YS). All the nonstress-relieved specimens exposed to salt spray and alternate immersion failed. Stress-relieved specimens (exposed to alternate immersion) failed at 75 and 90 percent of YS. No failures occurred at 50 percent of YS in the stress-relieved specimens which indicates a beneficial effect of the stress relief on the SCC resistance of these welds. The stress relief also had a positive effect on the mechanical properties of the welds (the most important being an increase of 21 percent on the YS). Under the conditions of these tests, the straight polarity plasma are welded HP 9Ni4Co-0.30C steel plate was found highly susceptible to SCC in the nonstress-relieved condition. This susceptibility to SCC was reduced by stress relieving.