Crack Development in Cross-Ply Laminates under Uniaxial Tension

摘要

This study addresses matrix-dominated failures in carbon fiber/polymer matrixcomposite laminates in a cross-ply lay-up. The events of interest are interlaminar fracture in the form of transverse cracks in the 90' plies and longitudinal splitting in the 0 deg plies and interlaminar fracture in the form of 0/90 delamination. These events were observed using various nondestructive evaluation (NDE) techniques during static tensile tests. Acoustic emission (AE) x radiography, and edge view microscopy were the principal ones utilized in a real-time environment. A comparison of the NDE results with an analytical model based on the classical linear fracture mechanics concept of strain energy release rate as a criterion for crack growth was performed. The virtual crack closure theory was incorporated with a finite element model to generate strain energy release rate curves for the analytical case. Celion carbon fiber/polyimide matrix (G30-500/PMR-15) was the material tested with cross-ply lay-ups of (0(2)/90(6))s and (0(4)/90(4))s. The test specimens contained thermally induced cracks caused by the high-temperature processing. The analytical model was updated to compensate for the initial damage and to study further accumulation by taking into account the crack interactions. By correlating the experimental and analytical data, the critical energy release rates were found for the observable events of interest.