Preliminary investigation of the potential for transient vapor release events during in situ vitrification based on thermal-hydraulic modeling

摘要

This study investigates a possible cause of molten glass displacements that occurred during two recent in situ vitrification (ISV) tests. The study was conducted for the US Department of Energy by Pacific Northwest Laboratory. It is hypothesized that these glass displacements are caused by large gas bubbles rising up through the ISV melt and bursting at its surface. These bubbles cause the molten surface to upwell and possibly overflow. When the bubbles burst, molten glass is thrown from the melt surface and the volume of gas contained in the bubble is released into the hood. Both of these phenomena are undesirable because the molten soil ejected from the melt is dangerous to operating personnel and can damage equipment. The sudden gas release can cause a temporary pressurization of the hood, allowing potentially contaminated gas to escape to the atmosphere. This study attempts to explain the conditions necessary for formation of large gas bubbles in the melt so that future glass displacements can be avoided.