Separate Assessment of Porosity and Uncombined Carbon in emented Carbides

摘要

Porosity and uncombined carbon in cemented carbides are traditionally assessed by comparison to standardized microstructure charts, such as those in ISO 4505-1978. To improve the accuracy in the characterization a fully automatic image analysis procedure has been developed. The analysis is performed using light optical microscopy on unetched polished specimens. The implemented algorithm separates uncombined carbon, C-defects, from pores, A- and B-defects. Pores are approximately distributed in a random way in the structure. Uncombined carbon is on the other hand precipitated into clusters of carbon particles. This difference is together with defect size used as a base for the separation. Small defects situated close together are classified as C-defects, small isolated defects as A-pores and large defects as B-pores. Pores are found to be more round than the somewhat elongated C-defects. The difference in shape is significant and can also be used as a separation criterion.Image analysis is used to quantitatively characterise the ISO 4505-1978 standard charts with respect to volume fraction, number density and size distribution of defects. The results are compared to measured distributions for true microstructures.