Nanoporous gold thin films synthesised via de-alloying of Au-based nanoglass for highly active SERS substrates

摘要

Nanoporous gold thin films have been fabricated through chemical de-alloying of Au-based nanoglass with a nanocolumnar structure, with composition Au40Cu28Ag7Pd5Si20 (at.%), that had previously been deposited by magnetron sputtering. By varying the de-alloying conditions, gold ligaments ranging from 20 to 100 nm were obtained. The microstructure and chemical composition of the as-prepared films were characterised by various techniques. Surfaceenhanced Raman scattering (SERS) of thin films was investigated using rhodamine 6G. The results indicate that the main microstructural features with interconnected ligaments and defects of nanoporous gold result in significant SERS enhancement.