Effect of Warm Rolling and Annealing on Microstructure, Texture, and Mechanical Properties of a 2205 Duplex Stainless Steel

摘要

>//rolling direction, RD) and a development of γ‐fiber (<111>//normal direction, ND), whereas the austenite has a reduction in the intensity of the {110}<112> brass component and a strengthening of the {110}<001> Goss and {112}<111> copper components. Multistage work hardening behavior is observed by Jaoul–Crussard analysis, which indicates the presence of secondary deformation mechanisms during the plastic deformation of the steel. Post‐deformation SEM and TEM results reveal the formation of α′ and ε‐martensite at deformed regions. The orientation relationship that develops between γ‐ and ε‐martensite is Shoji–Nishiyama (S–N) <110> ]]>_γ //2110 _ε .