Effects of CaCO3 additive on properties and microstructure of corundum- And mullite-based ceramic proppants

摘要

Corundum-mullite ceramic proppants have been successfully synthesized using raw materials of natural bauxite and solid waste coal gangue, CaCO3, as additive. The influences of calcium carbonate additive on phase composition, microstructure, and mechanical performances were systematically investigated. The results indicate that the addition of CaCO3 promotes the formation of liquid phase at lower temperature during sintering process, which is beneficial to the densification of the samples and the reduction of sintering temperature. Moreover, the mullite grains become finer and finer with the content of CaCO3 additive increasing, which improves the toughness and strength of the samples via a grain refinement strengthening mechanism. The ceramic proppants exhibit optimal performances with additive of 5 wt.% at 1350 degrees C, and the breakage ratio under 52 MPa closed pressure is the lowest. Additionally, the sintering temperature is dropped by 150 degrees C compared with the samples without adding calcium carbonate.