Fatigue behavior of magnesium alloy AJ91 studied by amplitude dependent damping measurements

摘要

The amplitude dependent damping of two bending beam samples of magnesium alloy AJ91 (9 wt.% Al, 1 wt.% Sr) was measured at room temperature in as cast condition, after quenching from high temperatures into water of room temperature and after various bending cycles to fatigue. Some measurements were performed successively with about 33 Hz and 100 Hz resonant frequency. The measurements show typical dislocation damping in as cast condition, after heat treatment at temperatures lower than 420°C, and cycle numbers lower then 50.000. For higher quenching temperatures the damping increases over the whole measured strain range with increasing quenching temperature and number of cycles to fatigue. After quenching from temperatures higher than 478°C the crack damping becomes dominant. The effects of damping seem to increase with increasing frequency. In one sample damping of individual cracks could be identified in the amplitude dependent damping curves by their characteristic course very similar to the ones postulated in an earlier publication by a simple rheological model [4]. The extending of crack length leads to a shift of the damping to lower strains.