Highly chemical ordered L1 _1 CoPt (111) films with perpendicular anisotropy grown on glass substrates

摘要

In this study, L1_1 CoPt (111) films were deposited on glass substrates at 300℃ with observed superlattice (111) and (333) peaks and easy axis distribution of 2°. The magnetic anisotropy constant was in the order of 10~7 erg/cm~3. The effect of CoPt layer thickness on domain structure and magnetic properties was investigated. With increasing film thickness, the squareness was reduced and the nucleation field changed from negative to positive, indicating low impedance to domain wall motion and increased demagnetizing energy. Magnetic force microscopy images demonstrated the magnetic domain structure changed from irregular and large domains to highly interconnected stripes with increasing CoPt layer thickness.