Effects of Sulfate on Tin Coatings Plated from Acid Tin Methanesulfonate Electrolytes

摘要

Methanesulphonic acid (MSA) invariably contains a certain amount of sulphate, formed during its manufacture. When used in elec-trodeposition solutions, methanesulphonic acid is typically used at concentrations of 5 to 20% of the total, from which it follows that sulphate is present in only trace amounts. The effects of sulphate ions in MSA on tin electrodeposition was studied, at concentrations up to 2.5 g/l. A small effect of sulphate is apparent in terms of metal deposition efficiency and the morphology of the deposit. At concentrations above 2.5 g/l, tin deposition is inhibited in the low c.d regions. Sulphate results in a change in the nucleation and growth processes, leading to a slightly rougher deposit.%Methansulfonsäure enthält herstellungsbedingt Sulfat in geringen Konzentrationen. Beim Einsatz für galvanische Elektrolyte ist Methansulfonsäure ein Bestandteil im Bereich zwischen 5 und 20%, woraus sich ein Sulfatanteil im Spurenbereich ergibt. Der Einfluss von Sulfat bis zu 2,5 g/l in Methansulfonatelektrolyten zur Abscheidung von Zinn wird untersucht. Eine geringe Auswirkung des Sulfatgehaltes zeigt sich auf die Metallausbeute und der Morphologie der Schichten. Die Zinnabscheidung wird bei Konzentrationen über 2,5 g/l im unteren Stromdichtebereich inhibiert. Sulfat verursacht eine Änderung bei der Keimbildung und dem Keimwachstum, woraus eine geringfügig rauere Abscheidung resultiert.