Effect of Metalloproteinase Inhibitors on the Microtensile Bond Strength of Composite Resin to Er:YAG Laser-Irradiated Dentin

摘要

This study evaluated the effect of matrix metalloproteinase (MMP) inhibitors - 2% (CHX) and sodium fluoride (NaF) (5000 ppm) - on microtensile bond strength (??TBS) of composite resin to Er:YAG laser-irradiated dentin after chemical degradation of the bond interface. The occlusal surface of forty sound human molars was removed exposing the dentin surface (n=10), which was polished, irradiated with Er:YAG laser, acid etched and dried. Twenty specimens were rewetted with 2% CHX (control group) and 20 were rewetted with NaF (5000 ppm). The adhesive system was applied and a 4-mm-high plateau of light-cured composite resin was built up. Resin-dentin sticks were obtained with a rectangular cross-sectional area (0.8-1 mm 2) and were either stored in water at 37 ?#61616;C for 24 h or submitted to chemical degradation. For chemical degradation, they were immersed in 10% NaOCl aqueous solution for 5 h and rinsed in water for 1 h. The sticks were submitted to microtensile test in a mechanical testing machine at 0.5 mm/min until failure. Fracture pattern was analyzed using SEM. ??TBS values were calculated in MPa and submitted to analysis of variance ANOVA (?±=0.05). The variance analysis showed that the 'MMP inhibitor' and 'degradation' factors (p=0.214 and p=0.093, respectively) and interaction between the factors were not statistically significant (p=0.143). Mixed failure predominated in all groups. In conclusion, the 2% CHX and NaF 5000 ppm presented similar ??TBS of composite resin to laser-irradiated dentin before and after chemical degradation