Effetto di additivi organici sulle proprieta delle fibre di allumina-zirconia ottenute per sol-gel

摘要

Alumina-zirconia fibres (Al_2O_3-10 wt.% ZrO_2) were prepared by the sol-gel method with organic additives viz. hydroxy ethyl cellulose (HEC) and polyvinyl alcohol (PVA). As the organic content is increased, the phase transition to α-Al_2O_3 is retarded in the presence of hydroxy ethyl cellulose and enhanced in the presence of polyvinyl alcohol. The phases present in the sintered fibres are α-Al_2O_3' t-ZrO_2 and m-ZrO_2. Infra red spectra of the sintered fibres show bands corresponding to α-Al_2O_3. The surface morphology of fibres prepared with higher amount of organics shows equiaxed grains with relatively dense microstructure for fibre prepared with hydroxy ethyl cellulose, whereas the structure is porous with polyvinyl alcohol. Tensile strength decreases with the increase in organic content.%Nella presente ricerca sono state preparate, con la tecnica sol-gel, fibre di alluminazirconia (10% in peso), utilizzando additivi organici quali idrossietilcellulosa (HEC) e polivinilacetato (PVA). All'aumentare del contenuto in idrossietilcellulosa, si è osservato un rallentamento nella trasformazione in α-Al_2O_3' mentre con polivinilacetato tale trasformazione è più rapida. Le fasi presenti nelle fibre sinterizzate sono α-Al_2O_3' t-ZrO_2 e m-ZrO_2. Gli spettri all'infrarosso delle fibre sinterizzate mostrano bande corrispondenti alla α-Al_2O_3. La microstruttura superficiale delle fibre preparate con la percentuale più elevata di idrossietilcellulosa (15% in peso), è caratterizzata da grani equiassiali ed elevata compattezza, mentre le fibre preparate con la medesima percentuale di polivinilacetato, presentano una porosità maggiore. La resistenza a trazione, in generale, diminuisce all'aumentare del contenuto organico.