Effect of annealing on phase transition in poly(vinylidene fluoride) films prepared using polar solvent

摘要

The γ-phase poly (vinylidene fluoride) (PVDF) films are usually prepared using dimethyl sulfoxide (DMSO) solvent, regardless of preparation temperature. Here we report the crystallization of both α and γ-phase PVDF films by varying preparation temperature using DMSO solvent. The γ-phase PVDF films were annealed at 70, 90, 110, 130 and 160°C for five hours. The changes in the phase contents in the PVDF at different annealing conditions have been described. When thin films were annealed at 90°C for 5 h, maximum percentage of β-phase appears in PVDF thin films. The γ-phase PVDF films completely converted to α-phase when they were annealed at 160°C for 5 h. From X-ray diffraction (XRD), Fourier transform infrared spectrum (FTIR), differential scanning calorimetry (DSC) and Raman studies, it is confirmed that the PVDF thin films, cast from solution and annealed at 90°C for 5 h, have maximum percentage of β-phase. The β-phase PVDF shows a remnant polarization of 4.9 μC/cm2 at 1400 kV/cm at 1 Hz.