Effect of Ceramic Thickness and Luting Agent Shade on the Color Masking Ability of Laminate Veneers

摘要

The main objective of the study was to recognize the effect of ceramic thickness and luting agent on the extent to which the restoration masks color variations that may be present in the underlying dental structure. Two pressable ceramics were used: Lithium disilicate reinforced (IPS e.max- Ivoclar Vivadent) and Leucite reinforced (Cergo- Dentsply). Fifteen ceramic discs were manufactured from each ceramic and divided into three groups, according to the thickness (0.5, 1, 1.5 mm). To simulate the color of a dark underlying dental structure, background discs, color C3, with 20 mm diameter, were made using resin composite. The ceramic discs with varying thicknesses were seated on the dark background of the resin composite with either resinous opaque cement or resinous cement. The color parameters were determined by the CIE Lab system of colors using a spectrophotometer and color differences (ΔE) were calculated. The results were then statistically analyzed, using ANOVA test and Tukey HSD test. The ΔE values of both ceramic systems were affected by both the luting agent and the ceramic thickness (P < 0.05). The use of an opaque luting agent resulted in an increase of the ΔE* values for all ceramics tested, regardless of the thickness. For the 1.5-mm thick veneers, higher values in the color parameters were obtained for both ceramic materials. The color masking ability of ceramics used for laminate veneers is significantly affected by the thickness of the ceramic and the shade of the luting agent used.