In this paper,simulating industrial leaching process of zinc calcine and refine zinc ferrite from slag.Product 1 contains 98％ zinc ferrite and silicon,aluminum,antimony and other trace impurity elements in crystal structure.After mechanical activation got product 2 has multipoint BET specific surface area is 2.8249 m2/g,the average pore radius of single point is 15.66nm,and graded size distribute within the scope of 0.448 ～ 1.002 um and 1.002 ～ 10.024 um are 27.93％ and 53.48％ respectively with correlation coefficient is 0.999943.Compared treatment effect of pure zinc ferrite,product 1 and 2 to rhodamine B under the same condition,the results show that the adsorption capability for rhodamine B of ferrite zinc powder body stronger after mechanical activation.Adsorption-desorption process is greatly influenced by microwave power when it is less than 500 w,and degradation effect of microwave catalytic more apparent when power above 500 w.%对锌焙砂硫酸浸出渣中铁酸锌进行分离提纯,得到铁酸锌含量达98％,晶体结构中含硅、铝、锑等微量杂质元素的产品1对其进行机械活化处理得相关系数为0.999943时的多点BET比表面积为2.8249 m2/g,单点平均孔半径为15.66 nm,0.448～1.002 μm和1.002 ～ 10.024 μm粒级范围内粒度分布分别为27.93％和53.48％的产品2对比纯铁酸锌、产品1及产品2同条件下对罗丹明B的处理效果,结果表明经机械活化铁酸锌粉体对罗丹明B吸附能力较强.微波功率低于500 W时,吸附-解吸过程受功率大小影响较大,微波功率大于500 W时,微波催化降解作用较明显.
展开▼