Effects of initial grain size and strain on grain boundary engineering of high-nitrogen CrMn austenitic stainless steel

摘要

18 Mn18 Cr0.5 N steel with an initial grain size of 28–177 μm was processed by 2.5%–20% cold rolling and annealing at 1000°C for 24 h,and the grain boundary character distribution was examined via electron backscatter diffraction.Low strain(2.5%) favored the formation of low-Σ boundaries.At this strain,the fraction of low-Σ boundaries was insensitive to the initial grain size.However,specimens with fine initial grains showed decreasing grain size after grain boundary engineering processing.The fraction of low-Σ boundaries and the(Σ9 + Σ27)/Σ3 value decreased with increasing strain; furthermore,the specimens with fine initial grain size were sensitive to the strain.Finally,the effects of the initial grain size and strain on the grain boundary engineering were discussed in detail.