带环氧基的超顺磁性高分子微球的制备及其性能表征

摘要

Micron-size superparamagnetic poly(styrene-divinylbenzene-glycidyl methacrylate) (PSt-DVB-GMA)spheres were prepared via a modified suspension copolymerization method. Oleic acid coated magnetite (Fe3O4)nanoparticles made by co-precipitation were first mixed with monomers of St, DVB, GMA, and benzoyl peroxide (BPO) to form oil in water suspension with the presence of poly(vinyl pyrrolidone) (PVP-K30) as a stabilizer.Then the temperature of mixture was increased at a controlled rate to obtain small and relatively uniform droplets.Finally, the copolymerization reaction was initiated by the decomposition of BPO. The morphology and properties of magnetic PSt-DVB-GMA microspheres were examined by SEM, TEM, VSM, XRD and FT-IR. The magnetic microspheres obtained have very small size (about 4-7μm) in diameter with narrow size distribution and superparamagnetic characteristics. Powder X-ray diffraction measurements show the inverse cubic spinel structure for the magnetite dispersed in polymer microspheres. FT-IR spectroscopy indicates extensive oxirane groups existed on the surface of magnetic PSt-DVB-GMA microspheres.