Polybenzimidazole Membranes Containing Benzimidazole Side Groups for High Temprature Polymer Electrolyte Membrane Fuel Cells

摘要

Polybenzimidazole (PBI) with a high molecular weight of 69, 000 was first synthesized. It was afterwards grafted with benzimidazole pendant groups on the backbones. The acid doped benzimidaozle grafted PBI membranes were investigated and characterized including fuel cell tests at elevated temperatures without humidification. At an acid doping level of 13.1 mol H_3PO_4 per average molar repeat unit, the PBI membranes with a benzimidazole grafting degree of 10.6% demonstrated a conductivity of 0.15 S cm~(-1) and a H_2-air fuel cell peak power density of 378 mW cm~(-2) at 180°C at ambient pressure without humidification.